- Viscosity (mixed) @ +25 °C: 15.000-20.000 mPa-s
- Mixing ratio: 1:1
- Processing time: ca. 30 min
- Curing time: ca. 2-3 h
- Specific weight: 1,1 g/cm³
- Solids content: 100 %
- Temperature resistance: -40 °C bis +120 °C
- Physical properties (in solid state)
Shore hardness: 78-80 (ASTM D 2240)
Tensile shear strength: 18-24 N/mm² (DIN 53283)
Shear strength: 3-5 N/mm² (ISO 4578)
Thermal conductivity: 0,1 (W/mk)
Coefficient of thermal expansion: 60-120 x 10 E^6 (1/k)
Dielectric strength: 50-90 (kv/mm)
Volume resistivity: 3-5 x 10 E^12 (Ohm/cm)
- Chemical properties
Chemical resistance: The chemical resistance was tested using an aluminum -aluminum compound after 7 days of curing at 25 ° C in the substances listed below immersed and checked for tensile shear strength.
Gasoline: 17 N/mm²
Acetic acid (10 %): 15 N/mm²
Xylene: 15 N/mm²
Lubricating oil (HD30): 17 N/mm²
Paraffin: 16 N/mm²
Water (23 °C): 16 N/mm²
Water (90 °C): 16 N/mm²
Preparation : The surfaces to be bonded should first be freed with a suitable for the particular material cleaner from dust , oil, grease and other contaminants .
Application : After mixing, the adhesive should be immediately applied to the surfaces to be bonded . Corner joints should be supported . At an adhesive thickness of 0.13 mm , the maximum adhesive strength develops .
- Storage and durability
Storage : Storage and transport at temperatures above +38 ° C and frost must be avoided .
Durability : The durability in unopened containers is 12 months . This requires storage between +13 ° C and +27 ° C. The shelf life can be extended by storage between +10 ° C and +18 ° C .