Hardener Aero EPH 161 (500 g)
[R11212505]

Hardener Aero EPH 161 (500 g)

Hardener for Epoxy Resin L and L 20, EP Gel coat colourless and Mould Resin P
Contains no formaldehyde and no paraformaldehyde
Epoxy Resin L
Processing time: 90 minutes
Mixing ratio:
100 : 25 parts by weight of resin to hardener
100 : 29 parts by volume of resin to hardener
Curing time: 24 h at room temperature, followed by hot curing for: approx. 10 h at 60 °C
Max. heat distortion temperature after annealing: 120 °C
Laminate structures for vehicle construction in combination with this product and epoxy resin L are approved by the TÜV-Süd. Process instructions/TÜV-Report (unfortunately only in German)
Epoxy Resin L 20
The combination of L 20 and Hardener EPH 161 yields a low-viscosity laminating resin that exhibits superior impregnating and wetting properties to glass, aramid, and carbon fibres. In conjunction with L 20, hardener EPH 161 results in a long service life for the resin compound with very high mechanical and dynamic strengths and perfect curing in both thick (> 2 cm) and thin (1,5 mm) laminates. Before they can obtain the specified mechanical properties, the laminates must be post-cured for about fifteen hours at 60 °C after their initial cold-curing period.
The system L 20 + EPH 161 is approved for the construction of gliders.
Processing time: 90 minutes
Mixing ratio:
100 : 25 parts by weight of resin to hardener
100 : 29 parts by volume of resin to hardener
Curing time: 24 h at room temperature, followed by post-curing: for 15 h at 60 °C
Gel coat colourless
Processing time: 90 minutes
Mixing ratio:
100 : 24 parts by weight EP Gel coat : Hardener EPH 161
Curing time: 24 h at room temperature, afterwards hot curing approx. 10 h/60 °C (recommended, but not necessary).
Max. heat distorsion temperature after annealing: approx. 120 °C
Mould resin P
Processing time: 90 minutes
Mixing ratio:
100 : 17 parts by weight Mould Resin P : Hardener EPH 161
Gelling time: approx. 4 h
Curing time: 24 h at roomtemperature, afterwards hot curing: approx. 15 h/60 °C
Please order resin L and L 20, gel coatcolourless and mould resin P separately

under request

Reviews

Quick Find

Shopping Cart

1 x	45 mm black plastic spinner for fixed propeller
1 x	BULLIT Wing 840 mm
1 x	Aluminium tube with fibreglass case ø35x1.5mm, 500mm
1 x	PVC 0,14 qmm servos wire Hitec/Mpx (5 m)
1 x	Electric spoiler 185 mm (2 pcs)
1 x	BULLIT Wing 1095 mm
1 x	PVC 0,14 qmm servos wire JR/Graupner (5 m)
1 x	Hardener Aero EPH 161 (500 g)
1 x	Carbon fibre tape 125 g/m², 3k, UD (50 mm) roll/ 20 m
1 x	ARAMID honeycomb 1300x2600x2 mm
1 x	36 mm white plastic spinner for fixed propeller
1 x	Bidule 111 3000 mm
1 x	Bidule 170 ARF 3.48 m
1 x	Astra (Top Model)
1 x	Canopy Sweet / Siesta
1 x	STANDOFF GAS ENGINE MOUNT 38 mm
1 x	Bidule 111 3000 mm Canopy
1 x	Avia (Top Model)
1 x	Glass fabric tape 130 g/m² (Silane, plain) 25 mm / 100M
1 x	Carbon fibre tape 200 g/m² (unidirectional) 50 mm
1 x	Carbon fibre tape 125 g/m², 3k, UD (50 mm) roll/ 50 m
1 x	Vacuum sealing tape, 2.5 x 12 mm (up to 140 °C) 15 m
1 x
1 x	Glass fabric tape 225 g/m² (Silane, plain) 40 mm
1 x	Vacuum bag, 1200 mm x 50 m
1 x	Glass fabric tape 225 g/m² (Silane, plain) 40 mm X 100m
1 x	AIREX® Sheets C 70.55 (YELLOW) 1200x550x6.0 mm (5 pcs)
1 x	AIREX® Sheets C 70.55 (YELLOW) 1200x550x2.0 mm (10 pcs)
1 x	Glass fabric tape 130 g/m² (Silane, plain) 25 mm / 50M
1 x	Cyanocrylate MD GA460 odourless 20g
1 x	Hardener Aero EPH 161 (250 g)
1 x	Glass fabric tape 225 g/m² (Silane, plain) 30 mm X 100m
1 x	Carbon fibre tape 125 g/m², 3k, UD (25 mm) roll/ 10 m
1 x	AIREX® Sheets C 70.55 (YELLOW) 1200x550x2.0 mm (20 pcs)
1 x	Release wax 250ml
1 x	Wing-connector: Glass / Carbon tube (26.5/25 x 25/23) x 1000 mm
1 x	Mixing tube for double syringes and cartridges (MR 1:1 and 2:1)
1 x	TeXtreme® Carbon tape 38 g/m² (IM, unidirectional) 20 mm x 100m
1 x	CA Glue fast 20g
1 x	Carbon roving DowAksa / 24k / 1600 tex

5,563.44EUR